FeCrAl 0cr23al5 eileamaid teasachaidh uèir chòmhnard &stiallle factaraidh
Ìre | 0Cr23Al5 |
Meud | tighead: 0.05-3mm leud: 4-250mm |
Uachdar | sgoltadh soilleir |
Cuideam | 1-3kg / rolla, a rèir luchd-ceannach a 'tomhas |
Resistivity | 1.3±0.05μΩ.m |
cruas (HV) | 180-210HV |
Leudachadh | ≥16% |
Ìre | An teòthachd as àirde | Resistivity | cruas | Neart tensile | Leudachadh |
0Cr13Al4 | 1050 ℃ | 1.25±0.05μΩ.m | 180-210HV | ≥550N/mm2 | ≥16 |
0Cr15Al5 | 1100 ℃ | 1.3±0.05μΩ.m | 180-210HV | ≥550N/mm2 | ≥16 |
0Cr21Al6Nb | 1300 ℃ | 1.42±0.05μΩ.m | 200-240HV | 750N/mm2 | ≥12 |
Cr20Ni80 | 1200 ℃ | 1.09±0.05μΩ.m | 180-220HV | 750N/mm2 | ≥20 |
Cr15Ni60 | 1150 ℃ | 1.12±0.05μΩ.m | 175-210HV | 750N/mm2 | ≥20 |
Cr20Ni35 | 1100 ℃ | 1.04±0.05μΩ.m | 180-220HV | 750N/mm2 | ≥20 |
Cr25Ni20(310S) | 1100 ℃ | 0.86±0.05μΩ.m | 180-220HV | 750N/mm2 | ≥20 |
Ìre | Co-dhèanamh ceimigeach % | ||||||||
C | P | S | Mn | Si | Cr | Ni | Al | Fe | |
≤ | |||||||||
0Cr15Al5 | 0.04 | 0.02 | 0.01 | 0.3 | ≤0.5 | 13-14 | <1 | 4.8-5.0 | cothromachadh |
0Cr21Al6Nb | 0.05 | 0.025 | 0.02 | 0.5 | ≤0.6 | 21-23 | ≤0.6 | 5-7 | cothromachadh |
0Cr13Al4 | 0.04 | 0.02 | 0.01 | 0.3 | ≤0.5 | 13-14 | <1 | 4.8-5.0 | cothromachadh |
Cr20Ni80 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.6 | 20-23 | cothromachadh | <0.5 | ≤1.0 |
Cr15Ni60 | 0.08 | 0.02 | 0.015 | 0.6 | 0.75-1.6 | 15-18 | 55-61 | <0.5 | cothromachadh |
Cr20Ni35 | 0.08 | 0.02 | 0.015 | 1.0 | 1-3 | 18-21 | 34-37 | - | cothromachadh |
Cr25Ni20 | 0.08 | 0.045 | 0.03 | 2.0 | 0.4-0.6 | 24-26 | 19-22 | - | cothromachadh |
Shanghai Tankii ALloy Stuth Co., Ltd.fòcas air cinneasachadh nichrome alloy, thermocouple uèir, fecral alloy, mionaideach alloy, copar nicil alloy, teirmeach stealladh alloy msaa ann an riochd uèir, duilleag, teip,stiall, slat agus truinnsear.
Tha sinn mar-thà air teisteanas siostam càileachd ISO 9001 fhaighinn agus aonta siostam dìon àrainneachd ISO 14001. Tha sealbh againn air seata iomlan de shruth toraidh adhartach de ghrinneachadh, lughdachadh fuachd, tarraing agus làimhseachadh teas msaa. Tha comas R&D neo-eisimeileach againn cuideachd gu pròiseil.