Co-dhèanamh àbhaisteach%
Ni | 75~76.5 | Fe | Bal. | Mn | 0.3~0.6 | Si | 0.15~0.3 |
Mo | - | Cu | 4.8~5.2 | Cr | 1.8~2.2 | ||
C | ≤0.03 | P | ≤0.02 | S | ≤0.02 |
Feartan meacanaigeach àbhaisteach
Neart toraidh | Neart teannachaidh | Leudachadh |
Mpa | Mpa | % |
980 | 1030 | 3~50 |
Feartan corporra àbhaisteach
Dlùths (g/cm3) | 8.6 |
Frith-sheasmhachd dealain aig 20ºC (Om * mm2 / m) | 0.55 |
Co-èifeachd leudachaidh loidhneach (20ºC ~ 200ºC) X10-6 / ºC | 10.3~11.5 |
Co-èifeachd magnetostriction sàthachaidh λθ/ 10-6 | 2.4 |
Puing Curie Tc/ºC | 400 |
Feartan magnetach aloidhean le treòiteachd àrd ann an raointean lag | |||||||
1J76 | Treòiteachd tùsail | Treòiteachd as àirde | Èigneachadh | Dian-inntrigidh magnetach sàthaichte | |||
Stiall/duilleag air a roiligeadh fuar. Tiughas, mm | μ0.08/ (mH/m) | μm/ (mH/m) | Hc/ (A/m) | BS/ T | |||
≥ | ≤ | ||||||
0.01 mm | 17.5 | 87.5 | 5.6 | 0.75 | |||
0.1~0.19 mm | 25.0 | 162.5 | 2.4 | ||||
0.2~0.34 mm | 28.0 | 225.0 | 1.6 | ||||
0.35~1.0 mm | 30.0 | 250.0 | 1.6 | ||||
1.1~2.5 mm | 27.5 | 225.0 | 1.6 | ||||
2.6~3.0 mm | 26.3 | 187.5 | 2.0 | ||||
uèir fuar-tharraingte | |||||||
0.1 mm | 6.3 | 50 | 6.4 | ||||
Bàr | |||||||
8-100 mm | 25 | 100 | 3.2 |
Modh làimhseachaidh teas 1J76 | |
Meadhanan teasachaidh | Falamh le cuideam fuigheallach nach eil nas àirde na 0.1Pa, haidridean le puing drùchd nach eil nas àirde na minus 40 ºC. |
Teòthachd agus ìre teasachaidh | 1100~1150ºC |
Ùine cumail | 3~6 |
Ìre fuarachaidh | Le 100 ~ 200 ºC / h air fhuarachadh gu 600 ºC, air fhuarachadh gu luath gu 300ºC |